High-strength wear-resistant material manufacturers; 13,426,466,772 13,426,466,772 Liangjing 
 HGM-60 high strength wear-resistant material 
 Product uses; 
 Slag ditch in the field of industrial construction, silos, hoppers, mine shafts and other wear-resistant surface layer of junction structures as well as workshop, warehouses, supermarkets, car parks, plazas, playgrounds and other non-metallic oxide aggregate concrete ground. 

 The requirements of construction and operation; 
 First step; a grass-roots treatment, clean the surface of base, no floating dust, gravel, laitance, grease, mold release agents and other debris. The basis of the three pre-construction, loose parts should be removed, the original surface two pairs of full blasting or cutting hair, increasing the surface roughness to increase bond strength 24 hours to fully wet the original concrete construction, one hour before the removal of stagnant water 4 buried concrete grass-roots planted plum nail plum nail, steel welding, 5 plum nail distance 300mm 
 The second step; preparation of a highly efficient interface agent smear, taking advantage of is dry, construction. 
 The third step; mixing of high-strength wear-resistant material; mixing a high-strength wear-resistant material, the amount of water shall be furnished with the certificate on the recommended amount of water added, stirring evenly. Water consumption can be adjusted appropriately in accordance with the environmental conditions and the actual situation, 2 recommend the use of mechanical stirring, the mixing time is generally 2-3 minutes, stirring the site should be as close as possible to the construction site, reducing transport distance. Four winter construction, the recommended 50 degrees Celsius hot water mixing, the temperature of the new spices to not less than 15 degrees Celsius. 5 field use is strictly prohibited in the high strength and wear-resistant compound mixed with additives and admixtures. 
 The fourth step; smooth calender; evenly with a brush or roller brushing the J-302 concrete and then pouring blends touch wear-resistant material to run the touch while the wet state steel knife layered, each layer thickness is not easy for more than 30mm, in the process of wiping the hard compaction. According to the actual situation, abrasive wipe Haonai 3-5 hours, steel spatula pressure light leveling. 
 The fifth step; immediately stamped within 30 minutes after the maintenance, high strength wear-resistant material calender leveling wet straw bags or rockwool, and keep the surface moist for at least 7 days. 


 Packaging specifications; 25KG / bag 
 Preservation; ventilated and dry, not to damp, storage for 6 months 